Ammonium Paratungstate Preparing Blue Tungsten Oxide Affecting Factors
Ammonium paratungstate preparing blue tungsten oxide affecting factors are listed as below:
1.Temperature. As the temperature going up, grain size of blue tungsten oxide changes a little and irregularly. It turns out the effect of temperature is not obvious. Oxide content and ammonia content fall down.
2.Feeding speed. Feeding speed mainly controls the reduction time. The faster the feeding speed is, the shorter the reduction time. As the prolong of reduction time, oxide and ammonia content reduces. But the temperature has larger influence than reduction time. Ammonium paratungstate cracks into crystal water and ammonia under high temperature and turns into yellow tungsten oxide. Yellow tungsten oxide which is under hydrogen reduction and turns into blue tungsten oxide.
3.Speed of rotary furnace. As the speed of rotary furnace goes up, blue tungsten oxide grain size will be more even. It is because material gets more contact with furnace and the heating surface is bigger. It increase the uniformity and distribution of grain size of blue tungsten oxide.
2.Feeding speed. Feeding speed mainly controls the reduction time. The faster the feeding speed is, the shorter the reduction time. As the prolong of reduction time, oxide and ammonia content reduces. But the temperature has larger influence than reduction time. Ammonium paratungstate cracks into crystal water and ammonia under high temperature and turns into yellow tungsten oxide. Yellow tungsten oxide which is under hydrogen reduction and turns into blue tungsten oxide.
3.Speed of rotary furnace. As the speed of rotary furnace goes up, blue tungsten oxide grain size will be more even. It is because material gets more contact with furnace and the heating surface is bigger. It increase the uniformity and distribution of grain size of blue tungsten oxide.